Cold Rolled Hot Dipped Galvanized Steel Plate
Galvanized steel plate is divided into ordinary electrolytic plate and fingerprint resistant electrolytic plate. Fingerprint resistant plate adds a fingerprint resistant treatment on the basis of ordinary electrolytic plate, which can resist sweat. It is generally used on parts without any treatment, and the brand is secc-n. Ordinary electrolytic board can be divided into phosphating board and passivation board. Phosphating is commonly used. The brand is secc-p, commonly known as P material.
|
Specfications
Product
|
Galvanized sheet /coil
|
Width
|
600--1500mm
|
Thickness
|
0.12-5mm
|
Length
|
6-12m or According To Customer's Demends
|
Zinc Coating
|
30g/m2—275g/m2
|
Spangle
|
Big spangle, normal spangle, small spangle, non-spangle |
Surface Treatment
|
Chromate, Galvanized, Skin Pass, Passivity and Oiled(un-oiled)
|
Steel Grade | Dx51D, Dx52D, Dx53D, DX54D, S220GD, S250GD, S280GD, S350GD, S350GD, S550GD; SGCC, SGHC, SGCH, SGH340, SGH400, SGH440, or Customer’sRequirement |
Capacity
|
15,000MT/Month
|
Edge
|
Mill edge, cut edge
|
Delivery Time | within 15-20 days after receive 30% deposit or depend on Quantity |
Payment Term | T/T, Irrevocable L/C at sight (30% deposit) |
Trade Term | EXW, FOB, CFR, CIF |
Chemical Composition
Specification | Grade | Chemical Composition(wt%) | ||||||
C | Mn | Ni | Cr | Mo | Ti | |||
ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 |
Properties
Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S (N/MM2) |
T.S (N/MM2) |
EL (%) |
HRB |
Specific Heat (J/g℃) |
Modulus of Elasticity (KN/mm2) | ||
ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications:316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.
316Ti: Mainly used for industrial components.
|