ASTM grade A572 hot cold rolled Galvanized Carbon Steel Plate
Galvanization is the process of applying a protective zinc coating to steel or iron, to prevent rusting. Due to the good corrosion resistance of hot sale galvanized steel coil, the source of zinc is relatively easy and relatively inexpensive, so the production of GI steel coil with spangles in stock is superior to other coated coils. In recent years, galvanized coils have been used more widely and are increasingly used in the automotive industry.
|
Specfications
Chemical Composition
Specification | Grade | Chemical Composition(wt%) | ||||||
C | Mn | Ni | Cr | Mo | Ti | |||
ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 |
Properties
Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S (N/MM2) |
T.S (N/MM2) |
EL (%) |
HRB |
Specific Heat (J/g℃) |
Modulus of Elasticity (KN/mm2) | ||
ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications:316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.
316Ti: Mainly used for industrial components.
|