ANSI ASTM a283 c grade 1018 hot rolled carbon steel sheet
|
Q390 is a low alloy high strength structural steel.
Good comprehensive mechanical properties, good weldability, cold and hot workability and corrosion resistance, C, D, E grade steel has good low temperature toughness.
Ships, boilers, pressure vessels, oil storage tanks, bridges, power station equipment, hoisting and transportation machinery and other welded structural parts with higher loads.
|
Product Paramenters
|
Thickness
|
3mm-300mm or as required
|
|
Standard
|
JIS, AiSi, ASTM, GB, DIN, BS,BV
|
|
Length
|
4m-12m or as required
|
|
Width
|
0.6m-3m or as required
|
|
Place of Origin
|
China
|
|
Application
|
Widely used in ship, automobile, Bridges, buildings, machinery, pressure vessels and other manufacturing industries
|
|
Certification
|
CE,ISO
|
|
Tolerance
|
Thickness: +/-0.02mm, Width:+/-2mm
|
|
Processing Service
|
Bending, Welding, Decoiling, Punching, Cutting, Customized
|
|
Technique
|
Hot Rolled, Cold Rolled
|
|
Surface Treatment
|
Clean, blasting and painting according to customer requirement
|
|
Packages
|
Sea Worthy Packing
|
|
Advantage
|
Strong Corrosion Resistance
|
|
Color
|
Customized
|
|
Feature
|
It is widely used in small tools, small components, iron wire, siderosphere, pull rod, ferrule, weld assembly, structural metal,
connecting rod, lifting hook, bolt, nut, spindle, mandrel, axle, chain wheel, gear, car coupler.
|
Chemical Composition
| Specification |
Grade |
Chemical Composition(wt%) |
| C |
Mn |
Ni |
Cr |
Mo |
Ti |
| ASTMJIS |
316L/022Cr17Ni12Mo2 |
≤0.03 |
≤2.0 |
10.0-14.0 |
16.0-18.0 |
2.0-3.0 |
- |
| JIS |
SUS316L |
≤0.03 |
≤2.0 |
12.0-15.0 |
16.0-18.0 |
2.0-3.0 |
- |
| ASTMJIS |
316Ti/SUS 316Ti |
≤0.08 |
≤2.0 |
10.0-14.0 |
16.0-18.0 |
2.0-3.0 |
5*(C+N)-0.7 |
Properties
| Spec |
Grade |
Mechanical Property |
Physical Property |
|
Y.S
(N/MM2)
|
T.S
(N/MM2)
|
EL
(%)
|
HRB |
Specific Heat
(J/g℃)
|
Modulus of Elasticity (KN/mm2) |
| ASTM/GB |
316L/022Cr17Ni12Mo2 |
≥170 |
≥485 |
≥40 |
≤95 |
0.5 |
193 |
| JIS |
SUS316L |
≥175 |
≥480 |
≥40 |
≤90 |
193 |
| ASTM |
316Ti |
≥205 |
≥515 |
≥40 |
≤95 |
0.5 |
200 |
Applications:
316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.
316Ti: Mainly used for industrial components.
|