MTC Carbon Steel Coil 0.8mm Hot Rolled Steel Coil ISO9001
|
In cold rolled process, the hot rolled coil is rolled below the recrystallization temperature, and the generally rolled steel is rolled at room temperature. Steel sheet with high silicon content has low brittleness and low plasticity, and needs to be preheated to 200 °C before cold rolling. |
Specfication:
|
Thickness
|
0.8mm-1.2mm, as your request
|
|||
|
Width
|
30-4000mm,or as your request ( regular width 1000mm, 1250mm, 1500mm )
|
|||
|
Coil ID
|
508mm or 610mm
|
|||
|
Coil Weight
|
3 - 8 ton or as your request
|
|||
|
Standard
|
ASTM EN DIN GB ISO JIS BA ANSI
|
|||
|
Steel Grade
|
Q195, Q215,Q235,Q345,ST37, A36,45# ,16Mn, SPHC,SGCC,CGCC
|
|||
|
Technique
|
Hot rolled cold rolled as your request
|
|||
|
Surface Treatment
|
Bare,Black,Oiled,Shot Blasted,Spray Paint,Coated,Galvanized,or as Your Request
|
|||
|
Application
|
Applies to appliances construction, machinery manufacturing, container manufacturing, shipbuilding, bridges, etc.
|
|||
|
Package
|
Standard Export packing(Plastic film in the first layer,second layer is Kraft paper. Third layer is galvanized sheet)
|
|||
|
Payment Term
|
T/T,L/C,Western Union,Paypal,Apple Pay,Google Pay,D/A,D/P,MoneyGram
|
|||
|
Remarks
|
Insurance per to Contract terms;
MTC will be handed on with shipping documents; We accept the third party certificatation test. |
|||
Chemical Composition
| Specification | Grade | Chemical Composition(wt%) | ||||||
| C | Mn | Ni | Cr | Mo | Ti | |||
| ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
| JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
| ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 | |
Properties
| Spec | Grade | Mechanical Property | Physical Property | ||||
|
Y.S (N/MM2) |
T.S (N/MM2) |
EL (%) |
HRB |
Specific Heat (J/g℃) |
Modulus of Elasticity (KN/mm2) | ||
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications:316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.
316Ti: Mainly used for industrial components.
|
Our products are sold all over the world, you can rest assured.